Influence of the calcination temperature on the activity of hydroxyapatite-supported palladium catalyst in the methane oxidation reaction
Fecha
2020-06-26Autor
Boukha, Zouhair
Cortés-Reyes, Marina
De Rivas Martín, Beatriz
Alemany, Luis J.
González Velasco, Juan Ramón
Metadatos
Mostrar el registro completo del ítem
Applied Catalysis B: Environmental 277 : (2020) // Art. Id. 19280
Resumen
In the present study, a series of four hydroxyapatite (HAP) supported palladium samples, with a Pd loading close to 0.5 %, obtained through their calcination at 773, 873, 973, or 1073 K has been investigated. These samples have been characterized using a wide battery of complementary techniques. From these studies, it was found that the rise of the calcination temperature induces a progressive dehydroxylation of the support and a structure evolution of the species containing Pd 2+ , from tetrahedral (Td) to square planar geometry (D 4h ). Moreover, this enhances markedly the metal-support interactions. For instance, at the highest temperature (1073 K), Pd particles were found encapsulated by a thin support layer. Consequently, two distinct reducible species have been identified; one of them manifests SMSI. This increase in the Pd-HAP interaction strength seems to (i) expand the HAP lattice, (ii) change the Pd 2+ coordination from Td to D 4h geometry, (iii) promote PdO reduction and (iv) suppress CO chemisorption. These entire properties do compensate the poor textural properties and benefit the efficiency and stability of the Pd active phase in methane oxidation reaction.